Investigation on Effect of Acid Wash with Thermocol Ball on Physical Properties of Knitted Garments Abstract Washing is considered as the final process of garments finishing. Acid washing is one kind of finishing treatment used for making sewn garments aesthetic, fashionable, soft, comfortable and also adding value to the final garments. This paper investigates the effect of the acid washing (with thermocol balls and potassium permanganate) on different physical properties of three knitted garments (Single Jersey 100% Cotton T-shirt, Single Jersey 95% Cotton 5% Spandex T-Shirt and 1 × 1 Rib100% Cotton T-Shirt). Typical washing procedures and techniques were followed and then physical properties were analyzed under standard condition. It is observed that fabric weight, CPI, WPI, spirality and shrinkage increase while bursting strength, stitch length absorbency decrease after washing treatment. pH of all the samples is under controlled and lies between 7 to 8. There is no change in pilling, colorfastness to wash, water and dry rubbing while a little bit decrease in wet rubbing. 1. Introduction Nowadays, faded textile products have become very popular among the young customers all over the world [1] . For this reason, textile manufacturers are trying to develop numerous techniques to improve the visual outlook of the sewn garments. Different denim washing techniques have been developed and used on different materials to create a large variety of designs for trendy denim garments and jeans. Nowadays along with denim washing knit garments such as T-shirt, Polo shirt, and trouser, are also washed by using different techniques such as enzymes wash, softener wash, Silicone wash, tie dye wash, pigment wash, caustic wash, etc. are used to create or enhance the physical and mechanical property changes. Acid washing in knitted garments is a new technique which is done by potassium permanganate and pumice stone or other substitutes. Potassium permanganate is an inorganic chemical compound with the chemical formula KMnO4 . It is a strong oxidizing agent and used to make color fading effect on sewn garments. Sometimes it is used at the point of hand sand area or without hand sand area. As it is a great oxidizing agent, after applying, it is necessary to neutralize the garments by any good neutralizing agent. Thermocol is a commercial name. In 1951, the researchers of a German company named BASF successfully restructured chemical bonding of polystyrene (a synthetic petroleum product) molecules and developed a substance named stretch polystyrene. This substance was named Thermocol, which nowadays is manufactured through a simple process. Thermoplastic granules are expanded through application of steam and air. Expanded granules become much larger in size but remain very light, formable, & rigid. Small thermocol balls (0.75 – 1 cm diameter) are being used as a substitute of pumice stone in garments finishing process. Elias et al. (2015) studied the effect of change in concentration of KMnO4 and processing time on physico-mechanical properties of denim jeans during acid washing. It was found that the tensile strength, seam strength, stiffness and fabric weight were decreased after application of potassium permanganate with increasing processing time during washing treatment while yarn count (Ne), EPI, PPI and dimensional change were increased. Solaiman et al. (2015) investigated the effect of three types of washing (enzyme, softener, Silicone) on Physical and Mechanical Properties on five types of following knitted garments: 100% cotton Single Jersey T-shirt, Slub Single Jersey T-shirt, Double Lacoste (5% Lycra) Polo shirt, Single jersey CVC (T-shirt) and PC single Jersey (T-shirt). The results showed that when enzyme wash was applied on the knit garments, it improved all the tested properties of knit garments, and it also reduced the hairy fibers from the fabric surface. Similar results were found in case of Silicone and softener wash as well. However, the effect of acid wash with thermocol balls and potassium permanganate on physico mechanical properties on knitted garments was not studied in the past research. In this present study, three knitted garments (Single Jersey 100% Cotton T-shirt, Single Jersey 95% Cotton 5% T-Shirt and 1 × 1 Rib100% Cotton T-Shirt) were washed with H3PO4, KMnO4 along with thermocol balls and various properties were analyzed according to standard methods. 2. Materials and Methods 2.1. Garments Samples Following three types of reactive dyed knitted garments were used for this research:- 1) Single Jersey (S/J) T-Shirt (100% cotton), GSM 140; 2) Single Jersey (S/J) T-Shirt (95% Cotton 5% Spandex), GSM 159; 3) 1 × 1 Rib T-Shirt (100% Cotton), GSM 138. 2.2. Chemicals Phosphoric acid (H3PO4, Yalong, China) and potassium permanganate (KMnO4, GC, China), Jet (an anionic detergent, Bangladesh). 2.3. Washing Machine § Before Brand Name―Ngai Shing Development Limited; § M/C capacity-20 kg; § RPM (Revolution per minute)―30 – 33 rpm; § Origin―Hong Kong. 2.4. Acid Washing At first make a solution (5% phosphoric acid and 15 g/L potassium permanganate) ↓ Thermocol balls are taken into the washing machine (Thermocol balls 0.1% on the weight of garment) ↓ Sprinkle the solution into the machine ↓ Run the machine for 5 min (For ensuring all the balls get wetted completely) ↓ Load the garments into the machine and washing process carried out for 15 min at normal temperature ↓ Unload the garments from the machine ↓ Cold wash by automatic washing machine (Front loading) Detergent 1 gm/L (For 10 min at 30˚C temperature) ↓ Drain the bath ↓ Neutralization with Sodium metabisulfite (3 gm/L for 5 min at 45˚C) ↓ Drain the bath ↓ Unload the garments on trolley ↓ Hydro extracting ↓ Drying the garments (By tumble dryer for 15 min at 70˚C temperature) ↓ Washed goods 2.5. Testing and Analysis Fabric weight was measured according to ASTM D 3776 method [30] and according to BS EN 14970-2006, stitch length was measured [31] . According to AATCC 8 standard both the dry and wet rub tests were done. For absorbency testing, AATCC 79 method was followed [33] . CPI and WPI of the fabric was calculated by counting the number of the Coarses and wales contents in 1 inch of the fabric. IS 1963 method was used for this measurement. According to ASTM D 2259, shrinkage of these sample garments were tested. Bursting strength of samples was measured by an automatic bursting strength tester. Samples are gradually set on the diaphragm, the automatic bursting strength tester, measures time, distortion, pressure & the flow rate to burst the fabric. It was done according to ASTM D3786. AATCC 81-2006 method was used for measuring PH of the fabric. Spirally (Dimensional change) was measured according to AATCC Test Method 187-2013. Pilling test of Single Jersey and Rib fabric was done according to ISO. Color fastness to washing and water were determined respectively according to ISO 105-C10 and ISO 105-E01. 3. Results and Discussions In this article, the change of physical and mechanical properties due to the washing treatment has been investigated. The overall results are shown in Table 1. From this table, it is seen that the weight of the fabric increases for each garments. This increase is high in case of 1 × 1 Rib garments (13.76%). Actually when the knitted garments are faced with frictional action due to the thermocol balls and rotating cylinder of the washing machine, a trace of solution of KMnO4 and H3PO4 also get penetrated into the fiber structure causing change in internal.
সূত্র: ইন্টারনেট (https://www.scirp.org/journal/)
তারিখ: ডিসেম্বর ১৫, ২০২৪
রেটিং করুনঃ ,